Effect of TEPA loading on the physicochemical properties of Si-MCM-41 by impregnation method

Ahmed, Sohail and Ramli, Anita and Yusup, Suzana (2012) Effect of TEPA loading on the physicochemical properties of Si-MCM-41 by impregnation method. In: UNSPECIFIED.

[img] PDF - Published Version
Restricted to Registered users only

955Kb

Abstract

Si-MCM-41 with highly ordered hexagonal pore arrangement was synthesized hydrothermally at 100 oC. The calcined Si-MCM-41 was then modified with Tetraethylenepentamine (TEPA) using impregnation method. By impregnation method calcined Si-MCM-41 was modified with 10, 20, 30, 40 and 50% (w/w) of Tetraethylenpentamine (TEPA). The physicochemical properties were studied by characterizing these samples with FTIR, TGA, XRD, and CHNS analysis. Results showed that Si-MCM-41 successfully modified with TEPA by impregnation method. FTIR results showed that all the characteristic peaks of Si-MCM-41 i.e. 794, 1080 and 1230 cm-1 were existed after modification which means that mesoporous frame work remain intact. TGA analysis showed that TEPA impregnated Si- MCM-41 samples have thermal stability in the range of 140 – 500 oC. XRD results showed that intensity of the peaks reduced as the Si-MCM-41 modified with TEPA, this showed that TEPA molecules attached in the pores and on the surface. CHNS analysis confirmed the presence of carbon and nitrogen in the modified samples due to presence of Tetraethylenepentamine.

Item Type:Conference or Workshop Item (UNSPECIFIED)
Subjects:Q Science > QD Chemistry
Departments / MOR / COE:Departments > Fundamental & Applied Sciences
ID Code:8665
Deposited By: Assoc Prof Dr Anita Ramli
Deposited On:13 Dec 2012 11:39
Last Modified:19 Jan 2017 08:21

Repository Staff Only: item control page

Document Downloads

More statistics for this item...